As Hot Extruded (M30) C36200 Brass
M30 C36200 brass is C36200 brass in the M30 (as hot extruded) condition. The graph bars on the material properties cards below compare M30 C36200 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
100 GPa 15 x 106 psi
Elongation at Break
20 %
Poisson's Ratio
0.31
Rockwell B Hardness
62
Shear Modulus
39 GPa 5.6 x 106 psi
Shear Strength
230 MPa 33 x 103 psi
Tensile Strength: Ultimate (UTS)
390 MPa 56 x 103 psi
Tensile Strength: Yield (Proof)
340 MPa 49 x 103 psi
Thermal Properties
Latent Heat of Fusion
170 J/g
Maximum Temperature: Mechanical
120 °C 240 °F
Melting Completion (Liquidus)
900 °C 1650 °F
Melting Onset (Solidus)
890 °C 1630 °F
Specific Heat Capacity
380 J/kg-K 0.090 BTU/lb-°F
Thermal Conductivity
120 W/m-K 67 BTU/h-ft-°F
Thermal Expansion
21 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
26 % IACS
Electrical Conductivity: Equal Weight (Specific)
28 % IACS
Otherwise Unclassified Properties
Base Metal Price
23 % relative
Density
8.2 g/cm3 510 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
45 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 39 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
74 MJ/m3
Resilience: Unit (Modulus of Resilience)
560 kJ/m3
Stiffness to Weight: Axial
6.9 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
13 points
Strength to Weight: Bending
14 points
Thermal Diffusivity
37 mm2/s
Thermal Shock Resistance
13 points
Alloy Composition
| Cu | 60 to 63 | |
| Zn | 32.4 to 36.5 | |
| Pb | 3.5 to 4.5 | |
| Fe | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.