As Hot Extruded (M30) C62300 Bronze
M30 C62300 bronze is C62300 bronze in the M30 (as hot extruded) condition. The graph bars on the material properties cards below compare M30 C62300 bronze to: wrought bronzes (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
22 %
Poisson's Ratio
0.34
Shear Modulus
43 GPa 6.2 x 106 psi
Shear Strength
360 MPa 53 x 103 psi
Tensile Strength: Ultimate (UTS)
580 MPa 84 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 34 x 103 psi
Thermal Properties
Latent Heat of Fusion
230 J/g
Maximum Temperature: Mechanical
220 °C 430 °F
Melting Completion (Liquidus)
1050 °C 1910 °F
Melting Onset (Solidus)
1040 °C 1910 °F
Specific Heat Capacity
440 J/kg-K 0.1 BTU/lb-°F
Thermal Conductivity
54 W/m-K 31 BTU/h-ft-°F
Thermal Expansion
18 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
12 % IACS
Electrical Conductivity: Equal Weight (Specific)
13 % IACS
Otherwise Unclassified Properties
Base Metal Price
28 % relative
Density
8.3 g/cm3 520 lb/ft3
Embodied Carbon
3.1 kg CO2/kg material
Embodied Energy
52 MJ/kg 22 x 103 BTU/lb
Embodied Water
390 L/kg 46 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
100 MJ/m3
Resilience: Unit (Modulus of Resilience)
240 kJ/m3
Stiffness to Weight: Axial
7.6 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
19 points
Strength to Weight: Bending
19 points
Thermal Diffusivity
15 mm2/s
Thermal Shock Resistance
20 points
Alloy Composition
| Cu | 83.2 to 89.5 | |
| Al | 8.5 to 10 | |
| Fe | 2.0 to 4.0 | |
| Ni | 0 to 1.0 | |
| Sn | 0 to 0.6 | |
| Mn | 0 to 0.5 | |
| Si | 0 to 0.25 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B150: Standard Specification for Aluminum Bronze Rod, Bar, and Shapes
ASTM B124: Standard Specification for Copper and Copper Alloy Forging Rod, Bar, and Shapes
ASTM B283: Standard Specification for Copper and Copper-Alloy Die Forgings (Hot-Pressed)
ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015