Drawn and Stress Relieved (HR50) C62300 Bronze
HR50 C62300 bronze is C62300 bronze in the HR50 (drawn and stress relieved) condition. It has the highest strength and lowest ductility compared to the other variants of C62300 bronze. The graph bars on the material properties cards below compare HR50 C62300 bronze to: wrought bronzes (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
18 %
Poisson's Ratio
0.34
Shear Modulus
43 GPa 6.2 x 106 psi
Shear Strength
390 MPa 57 x 103 psi
Tensile Strength: Ultimate (UTS)
630 MPa 92 x 103 psi
Tensile Strength: Yield (Proof)
310 MPa 46 x 103 psi
Thermal Properties
Latent Heat of Fusion
230 J/g
Maximum Temperature: Mechanical
220 °C 430 °F
Melting Completion (Liquidus)
1050 °C 1910 °F
Melting Onset (Solidus)
1040 °C 1910 °F
Specific Heat Capacity
440 J/kg-K 0.1 BTU/lb-°F
Thermal Conductivity
54 W/m-K 31 BTU/h-ft-°F
Thermal Expansion
18 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
12 % IACS
Electrical Conductivity: Equal Weight (Specific)
13 % IACS
Otherwise Unclassified Properties
Base Metal Price
28 % relative
Density
8.3 g/cm3 520 lb/ft3
Embodied Carbon
3.1 kg CO2/kg material
Embodied Energy
52 MJ/kg 22 x 103 BTU/lb
Embodied Water
390 L/kg 46 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
95 MJ/m3
Resilience: Unit (Modulus of Resilience)
430 kJ/m3
Stiffness to Weight: Axial
7.6 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points
Thermal Diffusivity
15 mm2/s
Thermal Shock Resistance
22 points
Alloy Composition
| Cu | 83.2 to 89.5 | |
| Al | 8.5 to 10 | |
| Fe | 2.0 to 4.0 | |
| Ni | 0 to 1.0 | |
| Sn | 0 to 0.6 | |
| Mn | 0 to 0.5 | |
| Si | 0 to 0.25 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B150: Standard Specification for Aluminum Bronze Rod, Bar, and Shapes
ASTM B124: Standard Specification for Copper and Copper Alloy Forging Rod, Bar, and Shapes
ASTM B283: Standard Specification for Copper and Copper-Alloy Die Forgings (Hot-Pressed)
ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015