EN 1.3533 (18NiCrMo14-6) Case-Hardening Bearing Steel

EN 1.3533 steel is an alloy steel formulated for primary forming into wrought products. 1.3533 is the EN numeric designation for this material. 18NiCrMo14-6 is the EN chemical designation.

It has a moderately high density among EN wrought alloy steels. In addition, it has a very high base cost and a very high electrical conductivity.

The properties of EN 1.3533 steel include three common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare EN 1.3533 steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

210 to 220

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

690 to 1420 MPa 100 to 210 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

440 °C 830 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2580 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

47 W/m-K 27 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.9 % IACS

Electrical Conductivity: Equal Weight (Specific)

9.0 % IACS

Otherwise Unclassified Properties

Base Metal Price

5.0 % relative

Density

7.9 g/cm3 490 lb/ft3

Embodied Carbon

1.8 kg CO2/kg material

Embodied Energy

25 MJ/kg 11 x 103 BTU/lb

Embodied Water

60 L/kg 7.1 gal/lb

Common Calculations

PREN (Pitting Resistance)

2.1

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

24 to 50 points

Strength to Weight: Bending

22 to 36 points

Thermal Diffusivity

13 mm2/s

Thermal Shock Resistance

20 to 42 points

Alloy Composition

Among alloy steels, the composition of EN 1.3533 steel is notable for including aluminum (Al) and copper (Cu). Aluminum is used to control grain size and to deoxidize. Deoxidizing is required to control the effects of some other alloying elements. Copper is used to improve corrosion resistance, and to add at least some degree of precipitation hardenability.

Iron (Fe)Fe 92.9 to 94.9
Nickel (Ni)Ni 3.3 to 3.8
Chromium (Cr)Cr 1.3 to 1.6
Manganese (Mn)Mn 0.4 to 0.7
Silicon (Si)Si 0 to 0.4
Molybdenum (Mo)Mo 0.15 to 0.25
Carbon (C)C 0.15 to 0.2
Copper (Cu)Cu 0 to 0.3
Aluminum (Al)Al 0 to 0.050
Sulfur (S)S 0 to 0.030
Phosphorus (P)P 0 to 0.025
Oxygen (O)O 0 to 0.0020

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

ISO 683-17: Heat-treated steels, alloy steels and free-cutting steels - Part 17: Ball and roller bearing steels

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015