EN 1.4434 (X2CrNiMoN18-12-4) Stainless Steel

EN 1.4434 stainless steel is an austenitic stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the solution annealed (AT) condition. 1.4434 is the EN numeric designation for this material. X2CrNiMoN18-12-4 is the EN chemical designation.

The graph bars on the material properties cards below compare EN 1.4434 stainless steel to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

200

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Elongation at Break

41 %

Fatigue Strength

270 MPa 40 x 103 psi

Impact Strength: V-Notched Charpy

90 J 67 ft-lb

Poisson's Ratio

0.28

Shear Modulus

79 GPa 11 x 106 psi

Shear Strength

450 MPa 66 x 103 psi

Tensile Strength: Ultimate (UTS)

660 MPa 96 x 103 psi

Tensile Strength: Yield (Proof)

310 MPa 45 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

420 °C 780 °F

Maximum Temperature: Mechanical

980 °C 1800 °F

Melting Completion (Liquidus)

1450 °C 2640 °F

Melting Onset (Solidus)

1400 °C 2560 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

15 W/m-K 8.7 BTU/h-ft-°F

Thermal Expansion

16 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.6 % IACS

Otherwise Unclassified Properties

Base Metal Price

21 % relative

Density

7.9 g/cm3 490 lb/ft3

Embodied Carbon

4.2 kg CO2/kg material

Embodied Energy

57 MJ/kg 24 x 103 BTU/lb

Embodied Water

160 L/kg 19 gal/lb

Common Calculations

PREN (Pitting Resistance)

32

Resilience: Ultimate (Unit Rupture Work)

220 MJ/m3

Resilience: Unit (Modulus of Resilience)

240 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

23 points

Strength to Weight: Bending

21 points

Thermal Diffusivity

4.0 mm2/s

Thermal Shock Resistance

15 points

Alloy Composition

Among wrought stainless steels, the composition of EN 1.4434 stainless steel is notable for containing comparatively high amounts of nickel (Ni) and molybdenum (Mo). Nickel is primarily used to achieve a specific microstructure. In addition, it has a beneficial effect on mechanical properties and certain types of corrosion. Molybdenum is used to facilitate tempering. In addition, it offers modest bonuses to a wide range of material properties.

Iron (Fe)Fe 59.2 to 69.9
Chromium (Cr)Cr 16.5 to 19.5
Nickel (Ni)Ni 10.5 to 14
Molybdenum (Mo)Mo 3.0 to 4.0
Manganese (Mn)Mn 0 to 2.0
Silicon (Si)Si 0 to 1.0
Nitrogen (N)N 0.1 to 0.2
Phosphorus (P)P 0 to 0.045
Carbon (C)C 0 to 0.030
Sulfur (S)S 0 to 0.015

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes

EN 10088-1: Stainless steels - Part 1: List of stainless steels

Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002

Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984

Advances in Stainless Steels, Baldev Raj et al. (editors), 2010