EN 1.4912 (X7CrNiNb18-10) Stainless Steel

EN 1.4912 stainless steel is an austenitic stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the solution annealed (AT) condition. 1.4912 is the EN numeric designation for this material. X7CrNiNb18-10 is the EN chemical designation.

The graph bars on the material properties cards below compare EN 1.4912 stainless steel to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

180

Elastic (Young's, Tensile) Modulus

200 GPa 28 x 106 psi

Elongation at Break

40 %

Fatigue Strength

200 MPa 29 x 103 psi

Impact Strength: V-Notched Charpy

90 J 67 ft-lb

Poisson's Ratio

0.28

Shear Modulus

77 GPa 11 x 106 psi

Shear Strength

420 MPa 60 x 103 psi

Tensile Strength: Ultimate (UTS)

610 MPa 88 x 103 psi

Tensile Strength: Yield (Proof)

230 MPa 33 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

520 °C 970 °F

Maximum Temperature: Mechanical

940 °C 1720 °F

Melting Completion (Liquidus)

1430 °C 2610 °F

Melting Onset (Solidus)

1390 °C 2530 °F

Specific Heat Capacity

480 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

16 W/m-K 9.0 BTU/h-ft-°F

Thermal Expansion

16 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.4 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.7 % IACS

Otherwise Unclassified Properties

Base Metal Price

20 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

3.8 kg CO2/kg material

Embodied Energy

55 MJ/kg 24 x 103 BTU/lb

Embodied Water

140 L/kg 17 gal/lb

Common Calculations

PREN (Pitting Resistance)

18

Resilience: Ultimate (Unit Rupture Work)

190 MJ/m3

Resilience: Unit (Modulus of Resilience)

130 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

22 points

Strength to Weight: Bending

20 points

Thermal Diffusivity

4.2 mm2/s

Thermal Shock Resistance

14 points

Alloy Composition

Among wrought stainless steels, the composition of EN 1.4912 stainless steel is notable for including niobium (Nb). Niobium is primarily used to improve yield strength, particularly at elevated temperatures.

Iron (Fe)Fe 64.6 to 73.6
Chromium (Cr)Cr 17 to 19
Nickel (Ni)Ni 9.0 to 12
Manganese (Mn)Mn 0 to 2.0
Niobium (Nb)Nb 0.4 to 1.2
Silicon (Si)Si 0 to 1.0
Carbon (C)C 0.040 to 0.1
Phosphorus (P)P 0 to 0.045
Sulfur (S)S 0 to 0.015

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

EN 10222-5: Steel forgings for pressure purposes - Part 5: Martensitic, austenitic and austenitic-ferritic stainless steels

EN 10088-1: Stainless steels - Part 1: List of stainless steels

Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002

Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984

Advances in Stainless Steels, Baldev Raj et al. (editors), 2010