EN 1.7139 (16MnCrS5) Chromium Steel

EN 1.7139 steel is an alloy steel formulated for primary forming into wrought products. 1.7139 is the EN numeric designation for this material. 16MnCrS5 is the EN chemical designation. It has a moderately low embodied energy and a moderately low base cost among EN wrought alloy steels.

The properties of EN 1.7139 steel include seven common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare EN 1.7139 steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

150 to 180

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

480 to 1390 MPa 70 to 200 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

420 °C 790 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2580 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

44 W/m-K 25 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.3 % IACS

Otherwise Unclassified Properties

Base Metal Price

2.2 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.2 x 103 BTU/lb

Embodied Water

51 L/kg 6.1 gal/lb

Common Calculations

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

17 to 49 points

Strength to Weight: Bending

17 to 35 points

Thermal Diffusivity

12 mm2/s

Thermal Shock Resistance

14 to 41 points

Alloy Composition

Among alloy steels, the composition of EN 1.7139 steel is notable for containing a comparatively high amount of manganese (Mn). Manganese is used to improve hardenability, hot workability, and surface quality. There is some loss of ductility and weldability, however.

Iron (Fe)Fe 96.8 to 98
Manganese (Mn)Mn 1.0 to 1.3
Chromium (Cr)Cr 0.8 to 1.1
Carbon (C)C 0.14 to 0.19
Silicon (Si)Si 0 to 0.3
Copper (Cu)Cu 0 to 0.25
Sulfur (S)S 0.020 to 0.040
Phosphorus (P)P 0 to 0.025

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

EN 10297-1: Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 1: Non-alloy and alloy steel tubes

EN 10263-3: Steel rod, bars and wire for cold heading and cold extrusion - Part 3: Technical delivery conditions for case hardening steels

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015