EN AC-43100-F Cast Aluminum

EN AC-43100-F is EN AC-43100 aluminum in the as-fabricated (no temper or treatment) condition. It has the lowest strength and highest ductility compared to the other variants of EN AC-43100 aluminum. The graph bars on the material properties cards below compare EN AC-43100-F to: Euronorm (EN) cast aluminums (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

60

Elastic (Young's, Tensile) Modulus

71 GPa 10 x 106 psi

Elongation at Break

2.5 %

Fatigue Strength

68 MPa 9.9 x 103 psi

Poisson's Ratio

0.33

Shear Modulus

27 GPa 3.9 x 106 psi

Tensile Strength: Ultimate (UTS)

180 MPa 27 x 103 psi

Tensile Strength: Yield (Proof)

97 MPa 14 x 103 psi

Thermal Properties

Latent Heat of Fusion

540 J/g

Maximum Temperature: Mechanical

170 °C 340 °F

Melting Completion (Liquidus)

600 °C 1100 °F

Melting Onset (Solidus)

590 °C 1090 °F

Specific Heat Capacity

900 J/kg-K 0.22 BTU/lb-°F

Thermal Conductivity

140 W/m-K 81 BTU/h-ft-°F

Thermal Expansion

22 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

37 % IACS

Electrical Conductivity: Equal Weight (Specific)

130 % IACS

Otherwise Unclassified Properties

Base Metal Price

9.5 % relative

Density

2.6 g/cm3 160 lb/ft3

Embodied Carbon

7.8 kg CO2/kg material

Embodied Energy

150 MJ/kg 63 x 103 BTU/lb

Embodied Water

1070 L/kg 130 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

3.9 MJ/m3

Resilience: Unit (Modulus of Resilience)

66 kJ/m3

Stiffness to Weight: Axial

15 points

Stiffness to Weight: Bending

54 points

Strength to Weight: Axial

20 points

Strength to Weight: Bending

28 points

Thermal Diffusivity

60 mm2/s

Thermal Shock Resistance

8.6 points

Alloy Composition

Aluminum (Al)Al 86.9 to 90.8
Silicon (Si)Si 9.0 to 11
Magnesium (Mg)Mg 0.2 to 0.45
Iron (Fe)Fe 0 to 0.55
Manganese (Mn)Mn 0 to 0.45
Titanium (Ti)Ti 0 to 0.15
Zinc (Zn)Zn 0 to 0.1
Copper (Cu)Cu 0 to 0.1
Nickel (Ni)Ni 0 to 0.050
Tin (Sn)Sn 0 to 0.050
Lead (Pb)Pb 0 to 0.050
Residualsres. 0 to 0.15

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

EN 1706: Aluminium and aluminium alloys. Castings. Chemical composition and mechanical properties

CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015