Extra-Hard (H06) C68800 Brass
H06 C68800 brass is C68800 brass in the H06 (extra hard) temper. The graph bars on the material properties cards below compare H06 C68800 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
3.0 %
Poisson's Ratio
0.32
Rockwell B Hardness
97
Rockwell Superficial 30T Hardness
83
Shear Modulus
41 GPa 5.9 x 106 psi
Shear Strength
460 MPa 67 x 103 psi
Tensile Strength: Ultimate (UTS)
810 MPa 120 x 103 psi
Tensile Strength: Yield (Proof)
720 MPa 110 x 103 psi
Thermal Properties
Latent Heat of Fusion
190 J/g
Maximum Temperature: Mechanical
160 °C 320 °F
Melting Completion (Liquidus)
960 °C 1770 °F
Melting Onset (Solidus)
950 °C 1740 °F
Specific Heat Capacity
400 J/kg-K 0.1 BTU/lb-°F
Thermal Conductivity
40 W/m-K 23 BTU/h-ft-°F
Thermal Expansion
19 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
18 % IACS
Electrical Conductivity: Equal Weight (Specific)
20 % IACS
Otherwise Unclassified Properties
Base Metal Price
26 % relative
Density
8.2 g/cm3 510 lb/ft3
Embodied Carbon
2.8 kg CO2/kg material
Embodied Energy
48 MJ/kg 21 x 103 BTU/lb
Embodied Water
350 L/kg 42 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
23 MJ/m3
Resilience: Unit (Modulus of Resilience)
2430 kJ/m3
Stiffness to Weight: Axial
7.3 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
27 points
Strength to Weight: Bending
24 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
27 points
Alloy Composition
| Cu | 70.8 to 75.5 | |
| Zn | 21.3 to 24.1 | |
| Al | 3.0 to 3.8 | |
| Co | 0.25 to 0.55 | |
| Fe | 0 to 0.2 | |
| Pb | 0 to 0.050 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993