Extra-Spring (H10) C43000 Brass
H10 C43000 brass is C43000 brass in the H10 (extra spring) temper. It has the highest strength and lowest ductility compared to the other variants of C43000 brass. The graph bars on the material properties cards below compare H10 C43000 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
3.0 %
Poisson's Ratio
0.33
Rockwell B Hardness
100
Rockwell Superficial 30T Hardness
86
Shear Modulus
42 GPa 6.0 x 106 psi
Shear Strength
410 MPa 59 x 103 psi
Tensile Strength: Ultimate (UTS)
710 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
550 MPa 79 x 103 psi
Thermal Properties
Latent Heat of Fusion
190 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
1030 °C 1880 °F
Melting Onset (Solidus)
1000 °C 1830 °F
Specific Heat Capacity
380 J/kg-K 0.091 BTU/lb-°F
Thermal Conductivity
120 W/m-K 69 BTU/h-ft-°F
Thermal Expansion
18 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
27 % IACS
Electrical Conductivity: Equal Weight (Specific)
28 % IACS
Otherwise Unclassified Properties
Base Metal Price
29 % relative
Density
8.6 g/cm3 540 lb/ft3
Embodied Carbon
2.8 kg CO2/kg material
Embodied Energy
46 MJ/kg 20 x 103 BTU/lb
Embodied Water
330 L/kg 39 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
20 MJ/m3
Resilience: Unit (Modulus of Resilience)
1350 kJ/m3
Stiffness to Weight: Axial
7.1 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
23 points
Strength to Weight: Bending
20 points
Thermal Diffusivity
36 mm2/s
Thermal Shock Resistance
25 points
Alloy Composition
| Cu | 84 to 87 | |
| Zn | 9.7 to 14.3 | |
| Sn | 1.7 to 2.7 | |
| Pb | 0 to 0.1 | |
| Fe | 0 to 0.050 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.