Extruded and Drawn (H50) C46400 Brass

H50 C46400 brass is C46400 brass in the H50 (extruded and drawn) temper. It has the second highest strength and second lowest ductility compared to the other variants of C46400 brass. The graph bars on the material properties cards below compare H50 C46400 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

100 GPa 15 x 106 psi

Elongation at Break

23 %

Poisson's Ratio

0.31

Shear Modulus

40 GPa 5.8 x 106 psi

Shear Strength

290 MPa 42 x 103 psi

Tensile Strength: Ultimate (UTS)

460 MPa 66 x 103 psi

Tensile Strength: Yield (Proof)

190 MPa 28 x 103 psi

Thermal Properties

Latent Heat of Fusion

170 J/g

Maximum Temperature: Mechanical

120 °C 250 °F

Melting Completion (Liquidus)

900 °C 1650 °F

Melting Onset (Solidus)

890 °C 1630 °F

Specific Heat Capacity

380 J/kg-K 0.092 BTU/lb-°F

Thermal Conductivity

120 W/m-K 67 BTU/h-ft-°F

Thermal Expansion

21 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

26 % IACS

Electrical Conductivity: Equal Weight (Specific)

29 % IACS

Otherwise Unclassified Properties

Base Metal Price

23 % relative

Calomel Potential

-400 mV

Density

8.0 g/cm3 500 lb/ft3

Embodied Carbon

2.7 kg CO2/kg material

Embodied Energy

47 MJ/kg 20 x 103 BTU/lb

Embodied Water

330 L/kg 39 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

84 MJ/m3

Resilience: Unit (Modulus of Resilience)

170 kJ/m3

Stiffness to Weight: Axial

7.2 points

Stiffness to Weight: Bending

20 points

Strength to Weight: Axial

16 points

Strength to Weight: Bending

16 points

Thermal Diffusivity

38 mm2/s

Thermal Shock Resistance

15 points

Alloy Composition

Copper (Cu)Cu 59 to 62
Zinc (Zn)Zn 36.3 to 40.5
Tin (Sn)Sn 0.5 to 1.0
Lead (Pb)Pb 0 to 0.2
Iron (Fe)Fe 0 to 0.1
Residualsres. 0 to 0.4

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM B21: Standard Specification for Naval Brass Rod, Bar, and Shapes

ASTM B124: Standard Specification for Copper and Copper Alloy Forging Rod, Bar, and Shapes

ASTM B283: Standard Specification for Copper and Copper-Alloy Die Forgings (Hot-Pressed)

Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001

Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993