Full-Hard (H04) C14520 Copper
H04 C14520 copper is C14520 copper in the H04 (full hard) temper. The graph bars on the material properties cards below compare H04 C14520 copper to: wrought coppers (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
120 GPa 17 x 106 psi
Elongation at Break
9.6 %
Poisson's Ratio
0.34
Shear Modulus
43 GPa 6.3 x 106 psi
Shear Strength
190 MPa 28 x 103 psi
Tensile Strength: Ultimate (UTS)
330 MPa 47 x 103 psi
Tensile Strength: Yield (Proof)
250 MPa 37 x 103 psi
Thermal Properties
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C 390 °F
Melting Completion (Liquidus)
1080 °C 1970 °F
Melting Onset (Solidus)
1050 °C 1920 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
320 W/m-K 190 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
85 % IACS
Electrical Conductivity: Equal Weight (Specific)
85 % IACS
Otherwise Unclassified Properties
Base Metal Price
33 % relative
Density
8.9 g/cm3 560 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
42 MJ/kg 18 x 103 BTU/lb
Embodied Water
310 L/kg 37 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
29 MJ/m3
Resilience: Unit (Modulus of Resilience)
280 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
10 points
Strength to Weight: Bending
12 points
Thermal Diffusivity
94 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
| Cu | 99.2 to 99.596 | |
| Te | 0.4 to 0.7 | |
| P | 0.0040 to 0.020 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B301: Standard Specification for Free-Cutting Copper Rod, Bar, Wire, and Shapes
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015