Half-Hard 201LN Stainless Steel
Half-hard AISI 201LN is AISI 201LN stainless steel in the half-hard temper. It has the highest strength and lowest ductility compared to the other variants of AISI 201LN stainless steel. The graph bars on the material properties cards below compare half-hard AISI 201LN to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
320
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
25 %
Fatigue Strength
540 MPa 78 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
680 MPa 98 x 103 psi
Tensile Strength: Ultimate (UTS)
1060 MPa 150 x 103 psi
Tensile Strength: Yield (Proof)
770 MPa 110 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
410 °C 770 °F
Maximum Temperature: Mechanical
880 °C 1610 °F
Melting Completion (Liquidus)
1410 °C 2570 °F
Melting Onset (Solidus)
1370 °C 2490 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.7 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.9 % IACS
Otherwise Unclassified Properties
Base Metal Price
12 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
38 MJ/kg 16 x 103 BTU/lb
Embodied Water
140 L/kg 17 gal/lb
Common Calculations
PREN (Pitting Resistance)
20
Resilience: Ultimate (Unit Rupture Work)
240 MJ/m3
Resilience: Unit (Modulus of Resilience)
1520 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
38 points
Strength to Weight: Bending
30 points
Thermal Diffusivity
4.0 mm2/s
Thermal Shock Resistance
23 points
Alloy Composition
| Fe | 67.9 to 73.5 | |
| Cr | 16 to 17.5 | |
| Mn | 6.4 to 7.5 | |
| Ni | 4.0 to 5.0 | |
| Cu | 0 to 1.0 | |
| Si | 0 to 0.75 | |
| N | 0.1 to 0.25 | |
| P | 0 to 0.045 | |
| C | 0 to 0.030 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010