Half-Hard and Stress Relieved (HR02) C66200 Brass

HR02 C66200 brass is C66200 brass in the HR02 (half-hard and stress relieved) temper. The graph bars on the material properties cards below compare HR02 C66200 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

110 GPa 16 x 106 psi

Elongation at Break

15 %

Poisson's Ratio

0.33

Shear Modulus

42 GPa 6.2 x 106 psi

Shear Strength

270 MPa 40 x 103 psi

Tensile Strength: Ultimate (UTS)

450 MPa 65 x 103 psi

Tensile Strength: Yield (Proof)

410 MPa 60 x 103 psi

Thermal Properties

Latent Heat of Fusion

200 J/g

Maximum Temperature: Mechanical

180 °C 360 °F

Melting Completion (Liquidus)

1070 °C 1950 °F

Melting Onset (Solidus)

1030 °C 1880 °F

Specific Heat Capacity

390 J/kg-K 0.092 BTU/lb-°F

Thermal Conductivity

150 W/m-K 87 BTU/h-ft-°F

Thermal Expansion

18 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

35 % IACS

Electrical Conductivity: Equal Weight (Specific)

36 % IACS

Otherwise Unclassified Properties

Base Metal Price

29 % relative

Density

8.7 g/cm3 540 lb/ft3

Embodied Carbon

2.7 kg CO2/kg material

Embodied Energy

43 MJ/kg 19 x 103 BTU/lb

Embodied Water

320 L/kg 38 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

66 MJ/m3

Resilience: Unit (Modulus of Resilience)

760 kJ/m3

Stiffness to Weight: Axial

7.2 points

Stiffness to Weight: Bending

19 points

Strength to Weight: Axial

14 points

Strength to Weight: Bending

15 points

Thermal Diffusivity

45 mm2/s

Thermal Shock Resistance

16 points

Alloy Composition

Copper (Cu)Cu 86.6 to 91
Zinc (Zn)Zn 6.5 to 12.9
Nickel (Ni)Ni 0.3 to 1.0
Tin (Sn)Sn 0.2 to 0.7
Phosphorus (P)P 0.050 to 0.2
Iron (Fe)Fe 0 to 0.050
Lead (Pb)Pb 0 to 0.050
Residualsres. 0 to 0.5

All values are % weight. Ranges represent what is permitted under applicable standards.