Hardened F2 Tool Steel
Hardened SAE-AISI F2 is SAE-AISI F2 steel in the hardened (H) condition. The graph bars on the material properties cards below compare hardened SAE-AISI F2 to: tool steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Poisson's Ratio
0.29
Rockwell C Hardness
73
Shear Modulus
73 GPa 11 x 106 psi
Tensile Strength: Ultimate (UTS)
2360 MPa 340 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Melting Completion (Liquidus)
1520 °C 2760 °F
Melting Onset (Solidus)
1470 °C 2690 °F
Specific Heat Capacity
460 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
42 W/m-K 24 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.5 % IACS
Otherwise Unclassified Properties
Base Metal Price
10 % relative
Density
8.1 g/cm3 500 lb/ft3
Embodied Carbon
2.3 kg CO2/kg material
Embodied Energy
32 MJ/kg 14 x 103 BTU/lb
Embodied Water
50 L/kg 6.0 gal/lb
Common Calculations
PREN (Pitting Resistance)
6.5
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
81 points
Strength to Weight: Bending
49 points
Thermal Diffusivity
11 mm2/s
Thermal Shock Resistance
71 points
Alloy Composition
| Fe | 92.6 to 95.4 | |
| W | 3.0 to 4.5 | |
| C | 1.2 to 1.4 | |
| Cr | 0.2 to 0.4 | |
| Mn | 0.1 to 0.5 | |
| Si | 0.1 to 0.5 | |
| P | 0 to 0.030 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A681: Standard Specification for Tool Steels Alloy
Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015