Heat Treated (+TH) 1.3576 Steel

EN 1.3576 +TH steel is EN 1.3576 steel in the heat treated (HT) condition. The graph bars on the material properties cards below compare EN 1.3576 +TH steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

200

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

23 %

Fatigue Strength

290 MPa 42 x 103 psi

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

420 MPa 61 x 103 psi

Tensile Strength: Ultimate (UTS)

670 MPa 97 x 103 psi

Tensile Strength: Yield (Proof)

410 MPa 59 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

420 °C 790 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

46 W/m-K 27 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.5 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.5 % IACS

Otherwise Unclassified Properties

Base Metal Price

3.4 % relative

Density

7.9 g/cm3 490 lb/ft3

Embodied Carbon

1.7 kg CO2/kg material

Embodied Energy

22 MJ/kg 9.4 x 103 BTU/lb

Embodied Water

53 L/kg 6.3 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

130 MJ/m3

Resilience: Unit (Modulus of Resilience)

440 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

24 points

Strength to Weight: Bending

22 points

Thermal Diffusivity

12 mm2/s

Thermal Shock Resistance

20 points

Alloy Composition

Iron (Fe)Fe 95.5 to 97.5
Nickel (Ni)Ni 1.6 to 2.0
Manganese (Mn)Mn 0.4 to 0.7
Chromium (Cr)Cr 0.35 to 0.65
Molybdenum (Mo)Mo 0.2 to 0.3
Carbon (C)C 0.17 to 0.23
Silicon (Si)Si 0 to 0.4
Copper (Cu)Cu 0 to 0.3
Aluminum (Al)Al 0 to 0.050
Sulfur (S)S 0 to 0.030
Phosphorus (P)P 0 to 0.025
Oxygen (O)O 0 to 0.0020

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ISO 683-17: Heat-treated steels, alloy steels and free-cutting steels - Part 17: Ball and roller bearing steels

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015