High Shearability (+S) 1.1244 Steel

EN 1.1244 +S steel is EN 1.1244 steel in the shearability treated condition. The graph bars on the material properties cards below compare EN 1.1244 +S steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

220

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Poisson's Ratio

0.29

Shear Modulus

72 GPa 10 x 106 psi

Tensile Strength: Ultimate (UTS)

770 MPa 110 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1450 °C 2650 °F

Melting Onset (Solidus)

1410 °C 2570 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

51 W/m-K 29 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.1 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.2 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.9 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.1 x 103 BTU/lb

Embodied Water

47 L/kg 5.6 gal/lb

Common Calculations

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

28 points

Strength to Weight: Bending

24 points

Thermal Diffusivity

14 mm2/s

Thermal Shock Resistance

25 points

Alloy Composition

Iron (Fe)Fe 98.1 to 99.2
Manganese (Mn)Mn 0.8 to 1.1
Carbon (C)C 0.65 to 0.75
Silicon (Si)Si 0 to 0.4
Copper (Cu)Cu 0 to 0.3
Aluminum (Al)Al 0 to 0.050
Sulfur (S)S 0 to 0.030
Phosphorus (P)P 0 to 0.025
Oxygen (O)O 0 to 0.0020

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ISO 683-17: Heat-treated steels, alloy steels and free-cutting steels - Part 17: Ball and roller bearing steels

Carbon Steel Handbook, D. Gandy, 2007

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015