High Shearability (+S) 1.3570 Steel

EN 1.3570 +S steel is EN 1.3570 steel in the shearability treated condition. It has the second highest strength compared to the other variants of EN 1.3570 steel. The graph bars on the material properties cards below compare EN 1.3570 +S steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

220

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

750 MPa 110 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

410 °C 780 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

46 W/m-K 27 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.2 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.3 % IACS

Otherwise Unclassified Properties

Base Metal Price

2.3 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.5 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.3 x 103 BTU/lb

Embodied Water

50 L/kg 5.9 gal/lb

Common Calculations

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

26 points

Strength to Weight: Bending

23 points

Thermal Diffusivity

13 mm2/s

Thermal Shock Resistance

22 points

Alloy Composition

Iron (Fe)Fe 97.1 to 98.9
Manganese (Mn)Mn 0.65 to 1.1
Chromium (Cr)Cr 0.4 to 0.75
Carbon (C)C 0.17 to 0.23
Silicon (Si)Si 0 to 0.4
Molybdenum (Mo)Mo 0.1 to 0.2
Copper (Cu)Cu 0 to 0.3
Aluminum (Al)Al 0 to 0.050
Sulfur (S)S 0 to 0.030
Phosphorus (P)P 0 to 0.025
Oxygen (O)O 0 to 0.0020

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ISO 683-17: Heat-treated steels, alloy steels and free-cutting steels - Part 17: Ball and roller bearing steels

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015