Hot Rolled (+U) 1.0411 Steel

EN 1.0411 +U steel is EN 1.0411 steel in the hot worked condition. It has the highest ductility compared to the other variants of EN 1.0411 steel. The graph bars on the material properties cards below compare EN 1.0411 +U steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

140

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

26 %

Fatigue Strength

200 MPa 29 x 103 psi

Poisson's Ratio

0.29

Reduction in Area

63 %

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

320 MPa 46 x 103 psi

Tensile Strength: Ultimate (UTS)

490 MPa 71 x 103 psi

Tensile Strength: Yield (Proof)

270 MPa 39 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2670 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

52 W/m-K 30 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.0 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.0 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.8 % relative

Density

7.9 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

18 MJ/kg 7.9 x 103 BTU/lb

Embodied Water

47 L/kg 5.6 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

110 MJ/m3

Resilience: Unit (Modulus of Resilience)

190 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

17 points

Strength to Weight: Bending

18 points

Thermal Diffusivity

14 mm2/s

Thermal Shock Resistance

16 points

Alloy Composition

Iron (Fe)Fe 98.7 to 99.1
Manganese (Mn)Mn 0.7 to 0.9
Carbon (C)C 0.18 to 0.22
Silicon (Si)Si 0 to 0.1
Aluminum (Al)Al 0.020 to 0.060
Phosphorus (P)P 0 to 0.025
Sulfur (S)S 0 to 0.025

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

EN 10263-2: Steel rod, bars and wire for cold heading and cold extrusion - Part 2: Technical delivery conditions for steels not intended for heat treatment after cold working

Carbon Steel Handbook, D. Gandy, 2007

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015