Normalized and Tempered (+NT) 1.1181 Steel

EN 1.1181 +NT steel is EN 1.1181 steel in the normalized and tempered condition. The graph bars on the material properties cards below compare EN 1.1181 +NT steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

160

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

19 %

Fatigue Strength

190 MPa 28 x 103 psi

Impact Strength: V-Notched Charpy

23 J 17 ft-lb

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

350 MPa 51 x 103 psi

Tensile Strength: Ultimate (UTS)

560 MPa 81 x 103 psi

Tensile Strength: Yield (Proof)

280 MPa 41 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

42 W/m-K 24 BTU/h-ft-°F

Thermal Expansion

11 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.2 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.3 % IACS

Otherwise Unclassified Properties

Base Metal Price

2.1 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.2 x 103 BTU/lb

Embodied Water

47 L/kg 5.6 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

90 MJ/m3

Resilience: Unit (Modulus of Resilience)

210 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

20 points

Strength to Weight: Bending

19 points

Thermal Diffusivity

11 mm2/s

Thermal Shock Resistance

19 points

Alloy Composition

Iron (Fe)Fe 97.4 to 99.18
Manganese (Mn)Mn 0.5 to 0.8
Carbon (C)C 0.32 to 0.39
Silicon (Si)Si 0 to 0.4
Chromium (Cr)Cr 0 to 0.4
Nickel (Ni)Ni 0 to 0.4
Molybdenum (Mo)Mo 0 to 0.1
Phosphorus (P)P 0 to 0.035
Sulfur (S)S 0 to 0.035

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

EN 10250-2: Open die steel forgings for general engineering purposes - Part 2: Non-alloy quality and special steels

EN 10269: Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties

Creep-Resistant Steels, Fujio Abe et al. (editors), 2008

Carbon Steel Handbook, D. Gandy, 2007

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015