Quarter-Hard 302 Stainless Steel
Quarter-hard AISI 302 is AISI 302 stainless steel in the quarter-hard temper. The graph bars on the material properties cards below compare quarter-hard AISI 302 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
300
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
14 %
Fatigue Strength
330 MPa 48 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
590 MPa 86 x 103 psi
Tensile Strength: Ultimate (UTS)
980 MPa 140 x 103 psi
Tensile Strength: Yield (Proof)
580 MPa 84 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
410 °C 780 °F
Maximum Temperature: Mechanical
710 °C 1300 °F
Melting Completion (Liquidus)
1420 °C 2590 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
16 W/m-K 9.4 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.8 % IACS
Otherwise Unclassified Properties
Base Metal Price
15 % relative
Calomel Potential
-70 mV
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
3.0 kg CO2/kg material
Embodied Energy
42 MJ/kg 18 x 103 BTU/lb
Embodied Water
140 L/kg 17 gal/lb
Common Calculations
PREN (Pitting Resistance)
19
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m3
Resilience: Unit (Modulus of Resilience)
840 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
35 points
Strength to Weight: Bending
28 points
Thermal Diffusivity
4.4 mm2/s
Thermal Shock Resistance
21 points
Alloy Composition
| Fe | 67.9 to 75 | |
| Cr | 17 to 19 | |
| Ni | 8.0 to 10 | |
| Mn | 0 to 2.0 | |
| Si | 0 to 0.75 | |
| C | 0 to 0.15 | |
| N | 0 to 0.1 | |
| P | 0 to 0.045 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010