Quarter-Hard (H01) C19500 Copper
H01 C19500 copper is C19500 copper in the H01 (quarter hard) temper. It has the second lowest strength and second highest ductility compared to the other variants of C19500 copper. The graph bars on the material properties cards below compare H01 C19500 copper to: wrought coppers (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
120 GPa 17 x 106 psi
Elongation at Break
23 %
Poisson's Ratio
0.34
Rockwell B Hardness
71
Rockwell Superficial 30T Hardness
66
Shear Modulus
44 GPa 6.3 x 106 psi
Shear Strength
290 MPa 42 x 103 psi
Tensile Strength: Ultimate (UTS)
460 MPa 66 x 103 psi
Tensile Strength: Yield (Proof)
360 MPa 52 x 103 psi
Thermal Properties
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C 390 °F
Melting Completion (Liquidus)
1090 °C 2000 °F
Melting Onset (Solidus)
1090 °C 1990 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
200 W/m-K 120 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
50 % IACS
Electrical Conductivity: Equal Weight (Specific)
51 % IACS
Otherwise Unclassified Properties
Base Metal Price
31 % relative
Density
8.9 g/cm3 560 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
42 MJ/kg 18 x 103 BTU/lb
Embodied Water
310 L/kg 37 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
96 MJ/m3
Resilience: Unit (Modulus of Resilience)
550 kJ/m3
Stiffness to Weight: Axial
7.3 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
14 points
Strength to Weight: Bending
15 points
Thermal Diffusivity
58 mm2/s
Thermal Shock Resistance
16 points
Alloy Composition
| Cu | 94.9 to 98.6 | |
| Fe | 1.0 to 2.0 | |
| Co | 0.3 to 1.3 | |
| Sn | 0.1 to 1.0 | |
| P | 0.010 to 0.35 | |
| Zn | 0 to 0.2 | |
| Al | 0 to 0.020 | |
| Pb | 0 to 0.020 | |
| res. | 0 to 0.2 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B465: Standard Specification for Copper-Iron Alloy Plate, Sheet, Strip, and Rolled Bar