Quarter-Hard (H01) C41300 Brass

H01 C41300 brass is C41300 brass in the H01 (quarter hard) temper. The graph bars on the material properties cards below compare H01 C41300 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

110 GPa 16 x 106 psi

Elongation at Break

24 %

Poisson's Ratio

0.33

Rockwell B Hardness

53

Rockwell Superficial 30T Hardness

54

Shear Modulus

42 GPa 6.1 x 106 psi

Shear Strength

260 MPa 38 x 103 psi

Tensile Strength: Ultimate (UTS)

360 MPa 52 x 103 psi

Tensile Strength: Yield (Proof)

310 MPa 46 x 103 psi

Thermal Properties

Latent Heat of Fusion

200 J/g

Maximum Temperature: Mechanical

180 °C 360 °F

Melting Completion (Liquidus)

1040 °C 1900 °F

Melting Onset (Solidus)

1010 °C 1850 °F

Specific Heat Capacity

380 J/kg-K 0.092 BTU/lb-°F

Thermal Conductivity

130 W/m-K 77 BTU/h-ft-°F

Thermal Expansion

18 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

30 % IACS

Electrical Conductivity: Equal Weight (Specific)

31 % IACS

Otherwise Unclassified Properties

Base Metal Price

29 % relative

Density

8.7 g/cm3 550 lb/ft3

Embodied Carbon

2.7 kg CO2/kg material

Embodied Energy

44 MJ/kg 19 x 103 BTU/lb

Embodied Water

320 L/kg 38 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

81 MJ/m3

Resilience: Unit (Modulus of Resilience)

440 kJ/m3

Stiffness to Weight: Axial

7.2 points

Stiffness to Weight: Bending

18 points

Strength to Weight: Axial

11 points

Strength to Weight: Bending

13 points

Thermal Diffusivity

40 mm2/s

Thermal Shock Resistance

13 points

Alloy Composition

Copper (Cu)Cu 89 to 93
Zinc (Zn)Zn 5.1 to 10.3
Tin (Sn)Sn 0.7 to 1.3
Lead (Pb)Pb 0 to 0.1
Iron (Fe)Fe 0 to 0.050
Residualsres. 0 to 0.5

All values are % weight. Ranges represent what is permitted under applicable standards.