Quenched and Tempered (+QT) 1.4110 Stainless Steel
EN 1.4110 +QT steel is EN 1.4110 stainless steel in the quenched and tempered condition. The graph bars on the material properties cards below compare EN 1.4110 +QT steel to: wrought martensitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
11 %
Fatigue Strength
730 MPa 110 x 103 psi
Poisson's Ratio
0.28
Rockwell C Hardness
53
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
1030 MPa 150 x 103 psi
Tensile Strength: Ultimate (UTS)
1720 MPa 250 x 103 psi
Tensile Strength: Yield (Proof)
1330 MPa 190 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
390 °C 730 °F
Maximum Temperature: Mechanical
790 °C 1460 °F
Melting Completion (Liquidus)
1440 °C 2630 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
30 W/m-K 17 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.8 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.2 % IACS
Otherwise Unclassified Properties
Base Metal Price
8.0 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
2.3 kg CO2/kg material
Embodied Energy
33 MJ/kg 14 x 103 BTU/lb
Embodied Water
110 L/kg 13 gal/lb
Common Calculations
PREN (Pitting Resistance)
16
Resilience: Ultimate (Unit Rupture Work)
180 MJ/m3
Resilience: Unit (Modulus of Resilience)
4550 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
62 points
Strength to Weight: Bending
41 points
Thermal Diffusivity
8.1 mm2/s
Thermal Shock Resistance
60 points
Alloy Composition
| Fe | 81.4 to 86 | |
| Cr | 13 to 15 | |
| Mo | 0.5 to 0.8 | |
| C | 0.48 to 0.6 | |
| Mn | 0 to 1.0 | |
| Si | 0 to 1.0 | |
| V | 0 to 0.15 | |
| P | 0 to 0.040 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012
Corrosion of Stainless Steels, A. John Sedriks, 1996
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010