Solution Annealed (+AT) 1.4303 Stainless Steel
EN 1.4303 +AT steel is EN 1.4303 stainless steel in the solution annealed (AT) condition. It has the lowest strength and highest ductility compared to the other variants of EN 1.4303 stainless steel.
The graph bars on the material properties cards below compare EN 1.4303 +AT steel to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
190
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
49 %
Fatigue Strength
220 MPa 32 x 103 psi
Impact Strength: V-Notched Charpy
98 J 73 ft-lb
Poisson's Ratio
0.28
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
420 MPa 61 x 103 psi
Tensile Strength: Ultimate (UTS)
590 MPa 85 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 33 x 103 psi
Thermal Properties
Latent Heat of Fusion
290 J/g
Maximum Temperature: Corrosion
410 °C 780 °F
Maximum Temperature: Mechanical
940 °C 1730 °F
Melting Completion (Liquidus)
1420 °C 2590 °F
Melting Onset (Solidus)
1380 °C 2510 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.7 BTU/h-ft-°F
Thermal Expansion
16 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
17 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
3.2 kg CO2/kg material
Embodied Energy
46 MJ/kg 20 x 103 BTU/lb
Embodied Water
150 L/kg 17 gal/lb
Common Calculations
PREN (Pitting Resistance)
19
Resilience: Ultimate (Unit Rupture Work)
230 MJ/m3
Resilience: Unit (Modulus of Resilience)
140 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points
Thermal Diffusivity
4.0 mm2/s
Thermal Shock Resistance
13 points
Alloy Composition
| Fe | 64.8 to 72 | |
| Cr | 17 to 19 | |
| Ni | 11 to 13 | |
| Mn | 0 to 2.0 | |
| Si | 0 to 1.0 | |
| N | 0 to 0.1 | |
| C | 0 to 0.060 | |
| P | 0 to 0.045 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10269: Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
Machining of Stainless Steels and Super Alloys: Traditional and Nontraditional Techniques, Helmi A. Youssef, 2016
EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010