Spheroidized (+AC) 1.7149 Steel

EN 1.7149 +AC steel is EN 1.7149 steel in the spheroidized condition. It has the lowest strength compared to the other variants of EN 1.7149 steel. The graph bars on the material properties cards below compare EN 1.7149 +AC steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

150

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Poisson's Ratio

0.29

Reduction in Area

68 %

Shear Modulus

73 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

500 MPa 73 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

420 °C 800 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2580 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

46 W/m-K 27 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.4 % IACS

Otherwise Unclassified Properties

Base Metal Price

2.3 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.5 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.3 x 103 BTU/lb

Embodied Water

52 L/kg 6.2 gal/lb

Common Calculations

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

18 points

Strength to Weight: Bending

18 points

Thermal Diffusivity

12 mm2/s

Thermal Shock Resistance

15 points

Alloy Composition

Iron (Fe)Fe 96.5 to 97.7
Manganese (Mn)Mn 1.1 to 1.4
Chromium (Cr)Cr 1.0 to 1.3
Carbon (C)C 0.17 to 0.22
Silicon (Si)Si 0 to 0.3
Copper (Cu)Cu 0 to 0.25
Sulfur (S)S 0.020 to 0.040
Phosphorus (P)P 0 to 0.025

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

EN 10263-3: Steel rod, bars and wire for cold heading and cold extrusion - Part 3: Technical delivery conditions for case hardening steels

Welding Metallurgy, 2nd ed., Sindo Kou, 2003

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015