Spheroidized and Cold Drawn (+AC+C) 1.6571 Steel

EN 1.6571 +AC+C steel is EN 1.6571 steel in the spheroidized and cold-drawn condition. The graph bars on the material properties cards below compare EN 1.6571 +AC+C steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

190

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

11 %

Fatigue Strength

310 MPa 45 x 103 psi

Poisson's Ratio

0.29

Reduction in Area

63 %

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

380 MPa 56 x 103 psi

Tensile Strength: Ultimate (UTS)

640 MPa 93 x 103 psi

Tensile Strength: Yield (Proof)

500 MPa 72 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

420 °C 790 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

40 W/m-K 23 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.5 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.6 % IACS

Otherwise Unclassified Properties

Base Metal Price

3.4 % relative

Density

7.9 g/cm3 490 lb/ft3

Embodied Carbon

1.7 kg CO2/kg material

Embodied Energy

22 MJ/kg 9.4 x 103 BTU/lb

Embodied Water

53 L/kg 6.4 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

67 MJ/m3

Resilience: Unit (Modulus of Resilience)

650 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

23 points

Strength to Weight: Bending

21 points

Thermal Diffusivity

11 mm2/s

Thermal Shock Resistance

19 points

Alloy Composition

Iron (Fe)Fe 95.3 to 97.1
Nickel (Ni)Ni 1.4 to 1.7
Chromium (Cr)Cr 0.6 to 0.9
Manganese (Mn)Mn 0.5 to 0.9
Molybdenum (Mo)Mo 0.25 to 0.35
Carbon (C)C 0.16 to 0.23
Silicon (Si)Si 0 to 0.3
Copper (Cu)Cu 0 to 0.25
Sulfur (S)S 0.020 to 0.040
Phosphorus (P)P 0 to 0.025

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

EN 10263-3: Steel rod, bars and wire for cold heading and cold extrusion - Part 3: Technical delivery conditions for case hardening steels

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015