UNS N06975 Nickel Alloy

N06975 nickel is a nickel alloy formulated for primary forming into wrought products. Cited properties are appropriate for the solution annealed (AT) condition. The graph bars on the material properties cards below compare N06975 nickel to: wrought nickels (top), all nickel alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

200 GPa 30 x 106 psi

Elongation at Break

45 %

Fatigue Strength

210 MPa 31 x 103 psi

Poisson's Ratio

0.28

Shear Modulus

80 GPa 12 x 106 psi

Shear Strength

470 MPa 68 x 103 psi

Tensile Strength: Ultimate (UTS)

660 MPa 96 x 103 psi

Tensile Strength: Yield (Proof)

250 MPa 36 x 103 psi

Thermal Properties

Latent Heat of Fusion

320 J/g

Maximum Temperature: Mechanical

1000 °C 1820 °F

Melting Completion (Liquidus)

1430 °C 2600 °F

Melting Onset (Solidus)

1380 °C 2510 °F

Specific Heat Capacity

460 J/kg-K 0.11 BTU/lb-°F

Thermal Expansion

13 µm/m-K

Otherwise Unclassified Properties

Base Metal Price

50 % relative

Density

8.3 g/cm3 520 lb/ft3

Embodied Carbon

8.9 kg CO2/kg material

Embodied Energy

120 MJ/kg 53 x 103 BTU/lb

Embodied Water

270 L/kg 32 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

240 MJ/m3

Resilience: Unit (Modulus of Resilience)

150 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

22 points

Strength to Weight: Bending

20 points

Thermal Shock Resistance

18 points

Alloy Composition

Nickel (Ni)Ni 47 to 52
Chromium (Cr)Cr 23 to 26
Iron (Fe)Fe 10.2 to 23.6
Molybdenum (Mo)Mo 5.0 to 7.0
Titanium (Ti)Ti 0.7 to 1.5
Copper (Cu)Cu 0.7 to 1.2
Manganese (Mn)Mn 0 to 1.0
Silicon (Si)Si 0 to 1.0
Carbon (C)C 0 to 0.030
Phosphorus (P)P 0 to 0.030
Sulfur (S)S 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

ASTM B582: Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Plate, Sheet, and Strip

ASTM B581: Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Rod

ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube

ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

Welding Metallurgy and Weldability of Nickel-Base Alloys, John C. Lippold et al., 2009

Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971

Nickel Alloys, Ulrich Heubner (editor), 1998