UNS S32001 Stainless Steel

S32001 stainless steel is a duplex stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the annealed condition.

It has a fairly low embodied energy among wrought duplex stainless steels. In addition, it has a moderately low base cost and a fairly low tensile strength.

The graph bars on the material properties cards below compare S32001 stainless steel to: wrought duplex stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Elongation at Break

28 %

Fatigue Strength

370 MPa 54 x 103 psi

Poisson's Ratio

0.28

Rockwell C Hardness

22

Shear Modulus

78 GPa 11 x 106 psi

Shear Strength

450 MPa 65 x 103 psi

Tensile Strength: Ultimate (UTS)

690 MPa 100 x 103 psi

Tensile Strength: Yield (Proof)

510 MPa 74 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

430 °C 800 °F

Maximum Temperature: Mechanical

970 °C 1780 °F

Melting Completion (Liquidus)

1420 °C 2580 °F

Melting Onset (Solidus)

1370 °C 2500 °F

Specific Heat Capacity

480 J/kg-K 0.12 BTU/lb-°F

Thermal Conductivity

15 W/m-K 8.6 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.2 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.6 % IACS

Otherwise Unclassified Properties

Base Metal Price

12 % relative

Density

7.7 g/cm3 480 lb/ft3

Embodied Carbon

2.6 kg CO2/kg material

Embodied Energy

37 MJ/kg 16 x 103 BTU/lb

Embodied Water

150 L/kg 18 gal/lb

Common Calculations

PREN (Pitting Resistance)

23

Resilience: Ultimate (Unit Rupture Work)

180 MJ/m3

Resilience: Unit (Modulus of Resilience)

660 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

25 points

Strength to Weight: Bending

23 points

Thermal Diffusivity

4.0 mm2/s

Thermal Shock Resistance

19 points

Alloy Composition

Among wrought stainless steels, the composition of S32001 stainless steel is notable for containing a comparatively high amount of manganese (Mn) and including copper (Cu). Manganese is used to improve ductility at elevated temperatures. It also permits a higher nitrogen content than would otherwise be possible. Copper is used to improve resistance to acids, and to improve formability.

Iron (Fe) 66.6 to 75.5
Chromium (Cr) 19.5 to 21.5
Manganese (Mn) 4.0 to 6.0
Nickel (Ni) 1.0 to 3.0
Silicon (Si) 0 to 1.0
Copper (Cu) 0 to 1.0
Molybdenum (Mo) 0 to 0.6
Nitrogen (N) 0.050 to 0.17
Phosphorus (P) 0 to 0.040
Carbon (C) 0 to 0.030
Sulfur (S) 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

Metallic Materials: Physical, Mechanical, and Corrosion Properties, Philip A. Schweitzer, 2003

Duplex Stainless Steels, Iris Alvarez-Armas and Suzanne Degallaix-Moreuil (editors), 2009

Duplex Stainless Steels: Microstructure, Properties and Applications, Robert N. Gunn (editor), 1997

ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications

Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012

Corrosion of Stainless Steels, A. John Sedriks, 1996

ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994

Advances in Stainless Steels, Baldev Raj et al. (editors), 2010