2024 Aluminum vs. Machinable Glass-ceramic
2024 aluminum and machinable glass-ceramic belong to fundamentally different material chemistries. 2024 aluminum is a metal, while machinable glass-ceramic is a ceramic material. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.
For each property being compared, the top bar is 2024 aluminum and the bottom bar is machinable glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 67 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 540 | |
| 84 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 790 |
| Thermal Conductivity, W/m-K | 120 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 23 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.0 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 46 | |
| 51 |
| Strength to Weight: Axial, points | 18 to 50 | |
| 8.8 |
| Strength to Weight: Bending, points | 25 to 49 | |
| 16 |
| Thermal Diffusivity, mm2/s | 46 | |
| 0.56 |
| Thermal Shock Resistance, points | 8.6 to 24 | |
| 4.3 |