2195 Aluminum vs. 2095 Aluminum
Both 2195 aluminum and 2095 aluminum are aluminum alloys. Both are furnished in the T8 temper. Their average alloy composition is basically identical.
For each property being compared, the top bar is 2195 aluminum and the bottom bar is 2095 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 70 |
| Elongation at Break, % | 9.3 | |
| 8.5 |
| Fatigue Strength, MPa | 190 | |
| 200 |
| Fracture Toughness, MPa-m1/2 | 30 | |
| 20 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 350 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 590 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 560 | |
| 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 210 |
| Melting Completion (Liquidus), °C | 660 | |
| 660 |
| Melting Onset (Solidus), °C | 550 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 910 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 31 |
| Density, g/cm3 | 3.0 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.6 | |
| 8.6 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
| Embodied Water, L/kg | 1470 | |
| 1470 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 54 | |
| 57 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2290 | |
| 2640 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 46 |
| Strength to Weight: Axial, points | 55 | |
| 65 |
| Strength to Weight: Bending, points | 53 | |
| 59 |
| Thermal Diffusivity, mm2/s | 49 | |
| 49 |
| Thermal Shock Resistance, points | 26 | |
| 31 |
Alloy Composition
| Aluminum (Al), % | 91.9 to 94.9 | |
| 91.3 to 94.9 |
| Copper (Cu), % | 3.7 to 4.3 | |
| 3.9 to 4.6 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.15 |
| Lithium (Li), % | 0.8 to 1.2 | |
| 0.7 to 1.5 |
| Magnesium (Mg), % | 0.25 to 0.8 | |
| 0.25 to 0.8 |
| Manganese (Mn), % | 0 to 0.25 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 to 0.12 | |
| 0 to 0.12 |
| Silver (Ag), % | 0.25 to 0.6 | |
| 0.25 to 0.6 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0.080 to 0.16 | |
| 0.040 to 0.18 |
| Residuals, % | 0 | |
| 0 to 0.15 |