354.0 Aluminum vs. EN 1.8868 Steel

354.0 aluminum belongs to the aluminum alloys classification, while EN 1.8868 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 354.0 aluminum and the bottom bar is EN 1.8868 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
190
Elongation at Break, % 2.4 to 3.0
25
Fatigue Strength, MPa 92 to 120
260
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 27
73
Tensile Strength: Ultimate (UTS), MPa 360 to 380
540
Tensile Strength: Yield (Proof), MPa 280 to 310
350

Thermal Properties

Latent Heat of Fusion, J/g 530
250
Maximum Temperature: Mechanical, °C 170
410
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 550
1420
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 130
48
Thermal Expansion, µm/m-K 21
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 110
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.4
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 7.8
1.6
Embodied Energy, MJ/kg 150
21
Embodied Water, L/kg 1070
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 8.6 to 9.8
120
Resilience: Unit (Modulus of Resilience), kJ/m3 540 to 670
330
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 52
24
Strength to Weight: Axial, points 37 to 39
19
Strength to Weight: Bending, points 42 to 44
19
Thermal Diffusivity, mm2/s 52
13
Thermal Shock Resistance, points 17 to 18
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.3 to 89.4
0
Boron (B), % 0
0 to 0.0050
Carbon (C), % 0
0 to 0.16
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 1.6 to 2.0
0 to 0.3
Iron (Fe), % 0 to 0.2
96.4 to 100
Magnesium (Mg), % 0.4 to 0.6
0
Manganese (Mn), % 0 to 0.1
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.25
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 8.6 to 9.4
0 to 0.4
Sulfur (S), % 0
0 to 0.0080
Titanium (Ti), % 0 to 0.2
0 to 0.030
Vanadium (V), % 0
0 to 0.060
Zinc (Zn), % 0 to 0.1
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0 to 0.15
0