354.0 Aluminum vs. EN 1.8965 Steel

354.0 aluminum belongs to the aluminum alloys classification, while EN 1.8965 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 354.0 aluminum and the bottom bar is EN 1.8965 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
190
Elongation at Break, % 2.4 to 3.0
16
Fatigue Strength, MPa 92 to 120
220
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 27
73
Tensile Strength: Ultimate (UTS), MPa 360 to 380
570
Tensile Strength: Yield (Proof), MPa 280 to 310
340

Thermal Properties

Latent Heat of Fusion, J/g 530
250
Maximum Temperature: Mechanical, °C 170
420
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 550
1420
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 130
39
Thermal Expansion, µm/m-K 21
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 110
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
3.0
Density, g/cm3 2.7
7.8
Embodied Carbon, kg CO2/kg material 7.8
1.8
Embodied Energy, MJ/kg 150
25
Embodied Water, L/kg 1070
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 8.6 to 9.8
78
Resilience: Unit (Modulus of Resilience), kJ/m3 540 to 670
300
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 52
24
Strength to Weight: Axial, points 37 to 39
20
Strength to Weight: Bending, points 42 to 44
19
Thermal Diffusivity, mm2/s 52
10
Thermal Shock Resistance, points 17 to 18
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.3 to 89.4
0 to 0.030
Carbon (C), % 0
0 to 0.19
Chromium (Cr), % 0
0.35 to 0.85
Copper (Cu), % 1.6 to 2.0
0.2 to 0.6
Iron (Fe), % 0 to 0.2
94.6 to 99
Magnesium (Mg), % 0.4 to 0.6
0
Manganese (Mn), % 0 to 0.1
0.45 to 1.6
Molybdenum (Mo), % 0
0 to 0.35
Nickel (Ni), % 0
0 to 0.7
Niobium (Nb), % 0
0 to 0.065
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 8.6 to 9.4
0 to 0.55
Sulfur (S), % 0
0 to 0.035
Titanium (Ti), % 0 to 0.2
0 to 0.12
Vanadium (V), % 0
0 to 0.14
Zinc (Zn), % 0 to 0.1
0
Zirconium (Zr), % 0
0 to 0.17
Residuals, % 0 to 0.15
0