356.0 Aluminum vs. 7050 Aluminum
Both 356.0 aluminum and 7050 aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 356.0 aluminum and the bottom bar is 7050 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 70 |
| Elongation at Break, % | 2.0 to 3.8 | |
| 2.2 to 12 |
| Fatigue Strength, MPa | 55 to 75 | |
| 130 to 210 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 140 to 190 | |
| 280 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 240 | |
| 490 to 570 |
| Tensile Strength: Yield (Proof), MPa | 100 to 190 | |
| 390 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 500 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 190 |
| Melting Completion (Liquidus), °C | 620 | |
| 630 |
| Melting Onset (Solidus), °C | 570 | |
| 490 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 860 |
| Thermal Conductivity, W/m-K | 150 to 170 | |
| 140 |
| Thermal Expansion, µm/m-K | 21 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 to 43 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 to 150 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.6 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1110 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.2 to 8.2 | |
| 10 to 55 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 70 to 250 | |
| 1110 to 1760 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 53 | |
| 45 |
| Strength to Weight: Axial, points | 17 to 26 | |
| 45 to 51 |
| Strength to Weight: Bending, points | 25 to 33 | |
| 45 to 50 |
| Thermal Diffusivity, mm2/s | 64 to 71 | |
| 54 |
| Thermal Shock Resistance, points | 7.6 to 11 | |
| 21 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 90.1 to 93.3 | |
| 87.3 to 92.1 |
| Chromium (Cr), % | 0 | |
| 0 to 0.040 |
| Copper (Cu), % | 0 to 0.25 | |
| 2.0 to 2.6 |
| Iron (Fe), % | 0 to 0.6 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0.2 to 0.45 | |
| 1.9 to 2.6 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 0.1 |
| Silicon (Si), % | 6.5 to 7.5 | |
| 0 to 0.12 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.060 |
| Zinc (Zn), % | 0 to 0.35 | |
| 5.7 to 6.7 |
| Zirconium (Zr), % | 0 | |
| 0.080 to 0.15 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |