MakeItFrom.com
Menu (ESC)

5070 Aluminum vs. ASTM A182 Grade F22V

5070 aluminum belongs to the aluminum alloys classification, while ASTM A182 grade F22V belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is ASTM A182 grade F22V.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
190
Elongation at Break, % 20
21
Fatigue Strength, MPa 150
320
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
74
Shear Strength, MPa 190
420
Tensile Strength: Ultimate (UTS), MPa 300
670
Tensile Strength: Yield (Proof), MPa 140
460

Thermal Properties

Latent Heat of Fusion, J/g 390
250
Maximum Temperature: Mechanical, °C 190
460
Melting Completion (Liquidus), °C 640
1470
Melting Onset (Solidus), °C 550
1430
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 130
39
Thermal Expansion, µm/m-K 24
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
4.2
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 8.8
2.5
Embodied Energy, MJ/kg 150
35
Embodied Water, L/kg 1170
61

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
120
Resilience: Unit (Modulus of Resilience), kJ/m3 150
570
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 31
24
Strength to Weight: Bending, points 37
22
Thermal Diffusivity, mm2/s 53
11
Thermal Shock Resistance, points 14
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
0
Boron (B), % 0
0 to 0.0020
Calcium (Ca), % 0
0 to 0.015
Carbon (C), % 0
0.11 to 0.15
Chromium (Cr), % 0 to 0.3
2.0 to 2.5
Copper (Cu), % 0 to 0.25
0 to 0.2
Iron (Fe), % 0 to 0.4
94.6 to 96.4
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0 to 0.25
Niobium (Nb), % 0
0 to 0.070
Phosphorus (P), % 0
0 to 0.015
Silicon (Si), % 0 to 0.25
0 to 0.1
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0 to 0.15
0 to 0.030
Vanadium (V), % 0
0.25 to 0.35
Zinc (Zn), % 0.4 to 0.8
0
Residuals, % 0 to 0.15
0