5383 Aluminum vs. 535.0 Aluminum

Both 5383 aluminum and 535.0 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is 5383 aluminum and the bottom bar is 535.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 85 to 110
70
Elastic (Young's, Tensile) Modulus, GPa 68
67
Elongation at Break, % 6.7 to 15
10
Fatigue Strength, MPa 130 to 200
70
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
25
Shear Strength, MPa 190 to 220
190
Tensile Strength: Ultimate (UTS), MPa 310 to 370
270
Tensile Strength: Yield (Proof), MPa 150 to 310
140

Thermal Properties

Latent Heat of Fusion, J/g 390
390
Maximum Temperature: Mechanical, °C 200
170
Melting Completion (Liquidus), °C 650
630
Melting Onset (Solidus), °C 540
570
Specific Heat Capacity, J/kg-K 900
910
Thermal Conductivity, W/m-K 130
100
Thermal Expansion, µm/m-K 24
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 29
23
Electrical Conductivity: Equal Weight (Specific), % IACS 97
79

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.6
Embodied Carbon, kg CO2/kg material 9.0
9.4
Embodied Energy, MJ/kg 160
160
Embodied Water, L/kg 1170
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 23 to 40
24
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 690
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
51
Strength to Weight: Axial, points 32 to 38
28
Strength to Weight: Bending, points 38 to 42
35
Thermal Diffusivity, mm2/s 51
42
Thermal Shock Resistance, points 14 to 16
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92 to 95.3
91.5 to 93.6
Beryllium (Be), % 0
0.0030 to 0.0070
Boron (B), % 0
0 to 0.0050
Chromium (Cr), % 0 to 0.25
0
Copper (Cu), % 0 to 0.2
0 to 0.050
Iron (Fe), % 0 to 0.25
0 to 0.15
Magnesium (Mg), % 4.0 to 5.2
6.2 to 7.5
Manganese (Mn), % 0.7 to 1.0
0.1 to 0.25
Silicon (Si), % 0 to 0.25
0 to 0.15
Titanium (Ti), % 0 to 0.15
0.1 to 0.25
Zinc (Zn), % 0 to 0.4
0
Zirconium (Zr), % 0 to 0.2
0
Residuals, % 0 to 0.15
0 to 0.15