5383-O Aluminum vs. Annealed 92-silver 8-tin-oxide
5383-O aluminum belongs to the aluminum alloys classification, while annealed 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.
For each property being compared, the top bar is 5383-O aluminum and the bottom bar is annealed 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 80 |
| Elongation at Break, % | 15 | |
| 32 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 | |
| 62 |
| Shear Strength, MPa | 190 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 230 |
| Tensile Strength: Yield (Proof), MPa | 150 | |
| 120 |