6070 Aluminum vs. Grade 21 Titanium

6070 aluminum belongs to the aluminum alloys classification, while grade 21 titanium belongs to the titanium alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is 6070 aluminum and the bottom bar is grade 21 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
140
Elongation at Break, % 5.6 to 8.6
9.0 to 17
Fatigue Strength, MPa 95 to 130
550 to 660
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 26
51
Shear Strength, MPa 220 to 240
550 to 790
Tensile Strength: Ultimate (UTS), MPa 370 to 380
890 to 1340
Tensile Strength: Yield (Proof), MPa 350
870 to 1170

Thermal Properties

Latent Heat of Fusion, J/g 410
410
Maximum Temperature: Mechanical, °C 160
310
Melting Completion (Liquidus), °C 650
1740
Melting Onset (Solidus), °C 570
1690
Specific Heat Capacity, J/kg-K 900
500
Thermal Conductivity, W/m-K 160
7.5
Thermal Expansion, µm/m-K 23
7.1

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
60
Density, g/cm3 2.7
5.4
Embodied Carbon, kg CO2/kg material 8.3
32
Embodied Energy, MJ/kg 150
490
Embodied Water, L/kg 1170
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 20 to 32
110 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 880 to 900
2760 to 5010
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
32
Strength to Weight: Axial, points 38
46 to 69
Strength to Weight: Bending, points 42 to 43
38 to 50
Thermal Diffusivity, mm2/s 65
2.8
Thermal Shock Resistance, points 16 to 17
66 to 100

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.6 to 98
2.5 to 3.5
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0 to 0.1
0
Copper (Cu), % 0.15 to 0.4
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.5
0 to 0.4
Magnesium (Mg), % 0.5 to 1.2
0
Manganese (Mn), % 0.4 to 1.0
0
Molybdenum (Mo), % 0
14 to 16
Niobium (Nb), % 0
2.2 to 3.2
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.17
Silicon (Si), % 1.0 to 1.7
0.15 to 0.25
Titanium (Ti), % 0 to 0.15
76 to 81.2
Zinc (Zn), % 0 to 0.25
0
Residuals, % 0 to 0.15
0 to 0.4