6110 Aluminum vs. AWS ERTi-1

6110 aluminum belongs to the aluminum alloys classification, while AWS ERTi-1 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is AWS ERTi-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
110
Elongation at Break, % 2.2
24
Fatigue Strength, MPa 120
120
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 26
41
Tensile Strength: Ultimate (UTS), MPa 500
240
Tensile Strength: Yield (Proof), MPa 500
170

Thermal Properties

Latent Heat of Fusion, J/g 410
420
Maximum Temperature: Mechanical, °C 170
320
Melting Completion (Liquidus), °C 640
1670
Melting Onset (Solidus), °C 600
1620
Specific Heat Capacity, J/kg-K 900
540
Thermal Conductivity, W/m-K 170
21
Thermal Expansion, µm/m-K 23
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 140
7.1

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
37
Density, g/cm3 2.8
4.5
Embodied Carbon, kg CO2/kg material 8.2
31
Embodied Energy, MJ/kg 150
510
Embodied Water, L/kg 1170
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
52
Resilience: Unit (Modulus of Resilience), kJ/m3 1770
140
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
35
Strength to Weight: Axial, points 51
15
Strength to Weight: Bending, points 51
19
Thermal Diffusivity, mm2/s 67
8.7
Thermal Shock Resistance, points 22
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
0
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 0.8
0 to 0.080
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0
Nitrogen (N), % 0
0 to 0.012
Oxygen (O), % 0
0.030 to 0.1
Silicon (Si), % 0.7 to 1.5
0
Titanium (Ti), % 0 to 0.15
99.773 to 99.97
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0