7049 Aluminum vs. EN AC-46500 Aluminum
Both 7049 aluminum and EN AC-46500 aluminum are aluminum alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 7049 aluminum and the bottom bar is EN AC-46500 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 | |
| 91 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 74 |
| Elongation at Break, % | 6.2 to 7.0 | |
| 1.0 |
| Fatigue Strength, MPa | 160 to 170 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 28 |
| Tensile Strength: Ultimate (UTS), MPa | 510 to 530 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 420 to 450 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 520 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 610 |
| Melting Onset (Solidus), °C | 480 | |
| 520 |
| Specific Heat Capacity, J/kg-K | 860 | |
| 880 |
| Thermal Conductivity, W/m-K | 130 | |
| 100 |
| Thermal Expansion, µm/m-K | 23 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 81 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 10 |
| Density, g/cm3 | 3.1 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 7.6 |
| Embodied Energy, MJ/kg | 140 | |
| 140 |
| Embodied Water, L/kg | 1110 | |
| 1030 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 to 34 | |
| 2.3 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1270 to 1440 | |
| 170 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 49 |
| Strength to Weight: Axial, points | 46 to 47 | |
| 26 |
| Strength to Weight: Bending, points | 46 to 47 | |
| 32 |
| Thermal Diffusivity, mm2/s | 51 | |
| 41 |
| Thermal Shock Resistance, points | 22 to 23 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 85.7 to 89.5 | |
| 77.9 to 90 |
| Chromium (Cr), % | 0.1 to 0.22 | |
| 0 to 0.15 |
| Copper (Cu), % | 1.2 to 1.9 | |
| 2.0 to 4.0 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 1.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 2.0 to 2.9 | |
| 0.050 to 0.55 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.55 |
| Nickel (Ni), % | 0 | |
| 0 to 0.55 |
| Silicon (Si), % | 0 to 0.25 | |
| 8.0 to 11 |
| Tin (Sn), % | 0 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.25 |
| Zinc (Zn), % | 7.2 to 8.2 | |
| 0 to 3.0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.25 |