90-silver 10-cadmium-oxide vs. Solder Alloy 701
Both 90-silver 10-cadmium-oxide and solder alloy 701 are otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-cadmium-oxide and the bottom bar is solder alloy 701.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 7.4 |
| Electrical Conductivity: Equal Volume, % IACS | 72 to 100 | |
| 14 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 64 to 91 | |
| 17 |
| Elongation at Break, % | 1.1 to 28 | |
| 37 |
| Strength to Weight: Axial, points | 7.0 to 11 | |
| 2.0 |
| Strength to Weight: Bending, points | 8.8 to 12 | |
| 4.3 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 400 | |
| 54 |