ACI-ASTM CA28MWV Steel vs. ASTM A182 Grade F12 Class 1

Both ACI-ASTM CA28MWV steel and ASTM A182 grade F12 class 1 are iron alloys. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is ASTM A182 grade F12 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
23
Fatigue Strength, MPa 470
180
Poisson's Ratio 0.28
0.29
Reduction in Area, % 27
50
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 1080
470
Tensile Strength: Yield (Proof), MPa 870
250

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 740
430
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
45
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.6
Embodied Energy, MJ/kg 44
21
Embodied Water, L/kg 100
52

Common Calculations

PREN (Pitting Resistance) 17
2.8
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
91
Resilience: Unit (Modulus of Resilience), kJ/m3 1920
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 38
17
Strength to Weight: Bending, points 30
17
Thermal Diffusivity, mm2/s 6.6
12
Thermal Shock Resistance, points 40
14

Alloy Composition

Carbon (C), % 0.2 to 0.28
0.050 to 0.15
Chromium (Cr), % 11 to 12.5
0.8 to 1.3
Iron (Fe), % 81.4 to 85.8
96.8 to 98.4
Manganese (Mn), % 0.5 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0.9 to 1.3
0.44 to 0.65
Nickel (Ni), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.045
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0