ACI-ASTM CA28MWV Steel vs. EN 1.4501 Stainless Steel

Both ACI-ASTM CA28MWV steel and EN 1.4501 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is EN 1.4501 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
250
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 11
27
Fatigue Strength, MPa 470
430
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 1080
830
Tensile Strength: Yield (Proof), MPa 870
600

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 380
450
Maximum Temperature: Mechanical, °C 740
1100
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 11
22
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.1
4.1
Embodied Energy, MJ/kg 44
57
Embodied Water, L/kg 100
180

Common Calculations

PREN (Pitting Resistance) 17
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
210
Resilience: Unit (Modulus of Resilience), kJ/m3 1920
870
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 38
29
Strength to Weight: Bending, points 30
25
Thermal Diffusivity, mm2/s 6.6
4.0
Thermal Shock Resistance, points 40
22

Alloy Composition

Carbon (C), % 0.2 to 0.28
0 to 0.030
Chromium (Cr), % 11 to 12.5
24 to 26
Copper (Cu), % 0
0.5 to 1.0
Iron (Fe), % 81.4 to 85.8
57.6 to 65.8
Manganese (Mn), % 0.5 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.9 to 1.3
3.0 to 4.0
Nickel (Ni), % 0.5 to 1.0
6.0 to 8.0
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0.9 to 1.3
0.5 to 1.0
Vanadium (V), % 0.2 to 0.3
0