ACI-ASTM CD3MWCuN Steel vs. ASTM Grade HC Steel
Both ACI-ASTM CD3MWCuN steel and ASTM grade HC steel are iron alloys. They have 89% of their average alloy composition in common.
For each property being compared, the top bar is ACI-ASTM CD3MWCuN steel and the bottom bar is ASTM grade HC steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 29 | |
| 6.0 |
| Fatigue Strength, MPa | 370 | |
| 96 |
| Poisson's Ratio | 0.27 | |
| 0.27 |
| Shear Modulus, GPa | 80 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 500 | |
| 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 310 |
| Maximum Temperature: Corrosion, °C | 450 | |
| 460 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1410 |
| Melting Onset (Solidus), °C | 1410 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 490 |
| Thermal Conductivity, W/m-K | 16 | |
| 17 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 22 | |
| 14 |
| Density, g/cm3 | 7.9 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 2.8 |
| Embodied Energy, MJ/kg | 58 | |
| 40 |
| Embodied Water, L/kg | 180 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 42 | |
| 29 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 21 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 | |
| 95 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 26 |
| Strength to Weight: Axial, points | 28 | |
| 16 |
| Strength to Weight: Bending, points | 24 | |
| 16 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 4.5 |
| Thermal Shock Resistance, points | 22 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.5 |
| Chromium (Cr), % | 24 to 26 | |
| 26 to 30 |
| Copper (Cu), % | 0.5 to 1.0 | |
| 0 |
| Iron (Fe), % | 56.6 to 65.3 | |
| 61.9 to 74 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 3.0 to 4.0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 6.5 to 8.5 | |
| 0 to 4.0 |
| Nitrogen (N), % | 0.2 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 2.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.040 |
| Tungsten (W), % | 0.5 to 1.0 | |
| 0 |