MakeItFrom.com
Menu (ESC)

ACI-ASTM CF3MN Steel vs. ASTM A182 Grade FR

Both ACI-ASTM CF3MN steel and ASTM A182 grade FR are iron alloys. They have 68% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is ASTM A182 grade FR.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
28
Fatigue Strength, MPa 250
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
72
Tensile Strength: Ultimate (UTS), MPa 580
490
Tensile Strength: Yield (Proof), MPa 290
360

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1010
410
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 19
3.3
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.9
1.6
Embodied Energy, MJ/kg 53
21
Embodied Water, L/kg 160
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
120
Resilience: Unit (Modulus of Resilience), kJ/m3 210
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
17
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 13
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 17 to 22
0
Copper (Cu), % 0
0.75 to 1.3
Iron (Fe), % 58.7 to 71.9
95.2 to 97.3
Manganese (Mn), % 0 to 1.5
0.4 to 1.1
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 13
1.6 to 2.2
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.040
0 to 0.050