ACI-ASTM CH20 Steel vs. EN 1.4421 Stainless Steel

Both ACI-ASTM CH20 steel and EN 1.4421 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.4421 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
11 to 17
Fatigue Strength, MPa 290
380 to 520
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 610
880 to 1100
Tensile Strength: Yield (Proof), MPa 350
620 to 950

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 15
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
12
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.7
2.6
Embodied Energy, MJ/kg 53
36
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 25
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
120 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 300
960 to 2270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
31 to 39
Strength to Weight: Bending, points 21
26 to 30
Thermal Diffusivity, mm2/s 3.7
4.4
Thermal Shock Resistance, points 15
31 to 39

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.060
Chromium (Cr), % 22 to 26
15.5 to 17.5
Iron (Fe), % 54.7 to 66
74.4 to 80.5
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.7
Nickel (Ni), % 12 to 15
4.0 to 5.5
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 0.8
Sulfur (S), % 0 to 0.040
0 to 0.020