ACI-ASTM CK20 Steel vs. EN 1.0038 Steel

Both ACI-ASTM CK20 steel and EN 1.0038 steel are iron alloys. They have 54% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.0038 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
110 to 120
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
23 to 25
Fatigue Strength, MPa 220
140 to 160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
380 to 430
Tensile Strength: Yield (Proof), MPa 260
200 to 220

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
49
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 62
19
Embodied Water, L/kg 190
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
72 to 88
Resilience: Unit (Modulus of Resilience), kJ/m3 170
110 to 130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
13 to 15
Strength to Weight: Bending, points 19
15 to 16
Thermal Diffusivity, mm2/s 3.7
13
Thermal Shock Resistance, points 13
12 to 13

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.23
Chromium (Cr), % 23 to 27
0 to 0.3
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 46.7 to 58
97.1 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.080
Nickel (Ni), % 19 to 22
0 to 0.3
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 2.0
0 to 0.55
Sulfur (S), % 0 to 0.040
0 to 0.045