ACI-ASTM CK20 Steel vs. EN 1.3533 Steel

Both ACI-ASTM CK20 steel and EN 1.3533 steel are iron alloys. They have 58% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.3533 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
690 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
440
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
47
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 25
5.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
1.8
Embodied Energy, MJ/kg 62
25
Embodied Water, L/kg 190
60

Common Calculations

PREN (Pitting Resistance) 26
2.1
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
24 to 50
Strength to Weight: Bending, points 19
22 to 36
Thermal Diffusivity, mm2/s 3.7
13
Thermal Shock Resistance, points 13
20 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.2
0.15 to 0.2
Chromium (Cr), % 23 to 27
1.3 to 1.6
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 46.7 to 58
92.9 to 94.9
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.5
0.15 to 0.25
Nickel (Ni), % 19 to 22
3.3 to 3.8
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.030