AISI 201L Stainless Steel vs. 90-silver 10-cadmium-oxide

AISI 201L stainless steel belongs to the iron alloys classification, while 90-silver 10-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.

For each property being compared, the top bar is AISI 201L stainless steel and the bottom bar is 90-silver 10-cadmium-oxide.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 7.7
10
Electrical Conductivity: Equal Volume, % IACS 2.4
72 to 100
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
64 to 91
Elongation at Break, % 22 to 46
1.1 to 28
Shear Strength, MPa 520 to 660
170 to 230
Strength to Weight: Axial, points 27 to 37
7.0 to 11
Strength to Weight: Bending, points 24 to 30
8.8 to 12
Tensile Strength: Ultimate (UTS), MPa 740 to 1040
260 to 400

Comparable Variants