AISI 204 Stainless Steel vs. 90-silver 10-cadmium-oxide
AISI 204 stainless steel belongs to the iron alloys classification, while 90-silver 10-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is AISI 204 stainless steel and the bottom bar is 90-silver 10-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.7 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 72 to 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 64 to 91 |
| Elongation at Break, % | 23 to 39 | |
| 1.1 to 28 |
| Shear Strength, MPa | 500 to 700 | |
| 170 to 230 |
| Strength to Weight: Axial, points | 27 to 40 | |
| 7.0 to 11 |
| Strength to Weight: Bending, points | 24 to 31 | |
| 8.8 to 12 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1100 | |
| 260 to 400 |